Highlights in MAGMAiron 5.5


Quantitative prediction of shrinkage related defects with a new powerful feeding model taking into account

  • Convective heat transport during solidification
  • The metallurgical state of the melt
  • Inoculation effects on precipitated eutectic graphite
  • Atmospheric and local metallostatic pressure on feeding flow
  • Graphite expansion and austenite shrinkage
  • Flow resistance in mushy zones during solidification
  • Impact of mold stability on porosity